High efficiency FinFET diode

ABSTRACT

Disclosed are a FinFET diode of high efficiency, designed to resolve the degradation problem with a conventional FinFET diode arising from reduced active area, and a method of fabrication. The FinFET diode has a doped substrate, two spaced-apart groups of substantially parallel, equally-spaced, elongated semiconductor fin structures, dielectric layers formed between the two groups and among the fin structures for insulation, a plurality of substantially equal-spaced and parallel elongated gate structures perpendicularly traversing both groups of the fin structures, and two groups of semiconductor strips respectively formed lengthwise upon the two groups of the fin structures. The two groups of semiconductor strips are doped to have opposite conductivity types, p-type and n-type. The FinFET diode further has metal contacts formed upon the semiconductor strips. In an embodiment, the semiconductor strips may be integrally formed with the fin structures by epitaxial growth and in-situ doped.

This application claims priority to U.S. Provisional Patent ApplicationSer. No. 61/747,764, filed on Dec. 31, 2012, the entire disclosure ofwhich is hereby incorporated herein by reference.

BACKGROUND

The semiconductor industry has progressed into nanometer technologyprocess nodes in pursuit of higher device density, higher performance,and lower costs. As this progression takes place, challenges from bothfabrication and design issues have resulted in the development ofthree-dimensional designs, such as fin-like field effect transistor(FinFET) devices. The use of FinFET devices has been gaining popularityin the semiconductor industry. FinFET devices offer several advantagesover traditional Metal-Oxide Semiconductor Field Effect Transistor(MOSFET) devices (also referred to as planar devices). These advantagesmay include better chip area efficiency, improved carrier mobility, andfabrication processing that is compatible with the fabricationprocessing of planar devices. Thus, it may be desirable to design anintegrated circuit (IC) chip using FinFET devices for a portion of, orthe entire IC chip.

A typical FinFET device is fabricated with a thin fin-like structurecalled a “fin”, extending from a substrate, and a gate provided over(e.g., wrapping around) the fin. The fin structure is made ofsemiconductor material, typically silicon, and if used as a transistor,has a current channel formed inside. When the FinFET device is used as atransistor, the gate is used to control the current in the channel.

A diode can be built on a FinFET structure using silicon-on-insulator(SOI) technology in a fashion generally identical to those built intoday's planar SOI technologies or bulk CMOS technologies. Compared tothe traditional planar semiconductor diodes, however, the diodesconstructed by using the FinFET structure have a shortcoming of reducedefficiency due to the degradation caused by the fin structures. Thepresence of plural fin structures in the FinFET diodes reduces theactive area for producing injection current, and thereby decreasesefficiency of the diodes, defined by injection current generated per aunit cell area.

Therefore, there is a need to provide a FinFET diode and a method tomanufacture the same that has a higher efficiency than the conventionalFinFET diodes.

BRIEF DESCRIPTION OF THE DRAWINGS

The present disclosure is best understood from the following detaileddescription when read with the accompanying figures. It is emphasizedthat, in accordance with the standard practice in the industry, variousfeatures are not drawn to scale and are used for illustration purposesonly. In fact, the dimensions of the various features may be arbitrarilyincreased or reduced for clarity of discussion.

FIGS. 1A and 1B are schematic top plan views of a traditional planardiode and a typical FinFET diode designed in the prior art,respectively;

FIG. 2 is a flowchart of a process for fabricating a FinFET diode ofhigh efficiency in accordance with aspects of the present disclosure;

FIGS. 3A-3I are schematic diagrams of a process for forming a FinFETdiode of high efficiency in accordance with aspects of the presentdisclosure;

FIG. 4 is a schematic top plan view of a FinFET diode of high efficiencymade in an aspect of the present disclosure;

FIG. 5 is a perspective cross-sectional view of a FinFET diode of highefficiency made in an aspect of the present disclosure; and

FIGS. 6A and 6B are computer simulation results for efficiency ofvarious embodiments of a FinFET diode made in an aspect of the presentdisclosure.

DETAILED DESCRIPTION

It is understood that the following disclosure provides many differentembodiments, or examples, for implementing different features of theinvention. Specific examples of components and arrangements aredescribed below to simplify the present disclosure. These are, ofcourse, merely examples and are not intended to be limiting. Forexample, the formation of a first feature over or on a second feature inthe description that follows may include embodiments in which the firstand second features are formed in direct contact, and may also includeembodiments in which additional features may be formed between the firstand second features, such that the first and second features may not bein direct contact. In addition, the present disclosure may repeatreference numerals and/or letters in the various examples. Thisrepetition is for the sake of simplicity and clarity and does not initself dictate a relationship between the various embodiments and/orconfigurations discussed. Moreover, various features may be arbitrarilydrawn in different scales for the sake of simplicity and clarity.

The various aspects of the present disclosure, illustrated in FIGS. 2-5,involve a process for fabricating a FinFET diode of high efficiency anda FinFET diode so made. It should be understood that the invention isapplicable to various semiconductor technologies, for example, siliconon insulator (SOI), complementary metal oxide semiconductor (CMOS),BiCMOS, bipolar, and silicon germanium (SiGe), as long as the FinFETdiode is electrically isolated from other such fins and the substrate.

Now referring to the figures, FIGS. 1A and 1B provide schematic top planviews of a first planar diode and a first FinFET diode, respectively.Just as a planar diode has two different implant regions 10 and 20 inFIG. 1A, doped by p-type and n-type dopants (impurities) to form a p-njunction therebetween, the FinFET diode shown in FIG. 1B, also has twooppositely doped regions 50 and 60 formed upon the fin structures 70 andbetween the gate structures 80. The black bars 15 and 55 schematicallydenote metal contacts to the doped regions for providing bias betweenthe two regions. For a FinFET diode, the gate structures are notelectrically active as in a transistor where they played active role ofcontrolling currents in the channels formed within the fin structures.

It is known that due to the presence of plural fin structures in theFinFET diodes, the active area for producing injection current becomesreduced, thereby decreasing the efficiency of the diodes, which isdefined by injection current generated per a unit cell area. Forexample, in the particular FinFET structure in FIG. 1B, which has a finwidth of 10 nanometer (“nm”), a gate spacing of 118 nm, a gate pitch 204nm, and fin pitch 48 nm, it can be calculated that the efficiencyreduces to about 20% as compared to a planar diode in FIG. 1A for thesame drawn area.

FIG. 2 is a flowchart of a process 200 for fabricating a FinFET diode ofhigh efficiency in accordance with aspects of the present disclosure.FIGS. 3A-3I are schematic diagrams illustrating the process 200 of FIG.2 in accordance with aspects of the present disclosure.

At step 210, a substrate is provided. FIG. 3A shows a schematiccross-sectional view of a layer of stack comprising a substrate 302, ahard mask layer 306, and a photoresist 304 formed or provided accordingto an aspect of the present disclosure.

In the present embodiment, the substrate 302 includes a singlesemiconducting material such as bulk silicon. Alternatively, thesubstrate 302 may comprise other suitable elementary semiconductingmaterials, such as germanium in crystal; a compound semiconductor, suchas silicon carbide, silicon germanium, gallium arsenic, galliumphosphide, indium phosphide, indium arsenide, and/or indium antimonide;or combinations thereof. The substrate 302 may also include an insulatorlayer on top of the semiconductor layer. The insulator layer comprisesany suitable material, including silicon oxide, sapphire, other suitableinsulating materials, and/or combinations thereof. An exemplaryinsulator layer may be a buried oxide layer (BOX). The insulator isformed by any suitable process, such as separation by implantation ofoxygen (SIMOX), oxidation, deposition, and/or other suitable process.Alternatively, the substrate 302 may further include anothersemiconductor layer on top of an insulator layer to form asilicon-on-insulator (SOI) substrate, which can be fabricated usingwafer bonding, and/or other suitable methods. The substrate 302 maycomprise any suitable crystallographic orientation (e.g., a (100),(110), (111), or (001) crystallographic orientation).

At step 220, one or more substantially parallel elongated semiconductorfin structures 310 are formed upon the substrate 302. The formation ofthe fin structures 310 is achieved by using a layer of photoresist 304and a hard mask layer 306 disposed upon the substrate 302 and suitableprocesses including deposition, photolithography, and/or etchingprocesses as depicted in FIGS. 3A and 3B.

The photoresist 304 may be any suitable material used in the art, suchas Poly(methyl methacrylate) (PMMA), Poly(methyl glutarimide) (PMGI),Phenol formaldehyde resin (DNQ/Novolac), SU-8, and may be eitherpositive or negative photoresist. These materials are all applied as aliquid and, generally, spin-coated to ensure uniformity of thickness.After prebaking, the photoresist layer 304 is exposed to an ultraviolet(UV), deep ultraviolet (DUV) or electron beam through a pattern via aphotomask. The exposure to light causes a chemical change that allowssome of the photoresist to be removed by a special solution, called“developer” by analogy with photographic developer. For positivephotoresist, the most common type, the exposed part becomes soluble inthe developer. After going through a post-exposure baking process, theremaining (unexposed) parts of the photoresist 304 form a mask thatresists etching. FIG. 3A shows such photoresist masks 304 that resultedfrom the exposure, developing, and post-exposure baking process. In theembodiment shown in FIG. 3A, the photoresist masks 304 are patterned toconform to substantially parallel, equal-spaced, and elongated finstructures 310 to be produced in the subsequent step. In an embodimentof the present disclosure, the fin structures 310 to be formed on thesubstrate 302 may be divided into two groups of multiple, equal numberedfin structures, one for forming an implant region of a p-type thereon,and the other for forming an n-typed doping region thereon. Andpreferably, the two groups of the fin structures may be separated fromeach other such that their separation may be greater than the averagespacing among the fin structures within each group. Accordingly, asshown in FIG. 3A, the photoresist masks 304 may be patterned into twogroups, corresponding to two doping regions of opposite implantationtypes, with a gap between the two groups that is greater than theinter-spacing of the masks 304. The photoresist masks 304 may then beused to etch the fin structure 310 into the silicon layer.

The hard mask layer 306 is needed to form dielectric strips between thefin structures 310 for insulation in a later step, and may be formedupon the substrate 302 and below the photoresist masks 304 by anysuitable process. It may be composed of silicon nitride (Si₃Ni₄) or anysuitable material, such as SiON, SiC, SiOC, spin-on glass (SOG), a low-kfilm, tetraethylorthosilicate (TEOS), plasma enhanced CVD oxide(PE-oxide), high-aspect-ratio-process (HARP) formed oxide, and/or othersuitable material.

After forming the photoresist masks 304 and a hard mask layer 306 asshown in FIG. 3A, the fin structures 310 are formed out of the substrate302 by etching the hard mask layer 306 and the substrate 302 usingreactive ion etching (RIE) processes and/or other suitable processes. Asshown in FIG. 3B, portions of the hard mask layer 306 and the substrate302 that lie under the photoresist masks 304 survive the etching asshown in FIG. 3B. The surviving portions of silicon substrate 302 formthe silicon fin structures 310, the surviving portions of the hard masklayer 306 become spacers for the layer of dielectric insulation to befilled among the fin structures 310, and the etched-out portions definethe trenches 315.

In another example, silicon fin structures 310 may be formed bypatterning and etching a silicon layer deposited overlying an insulatorlayer (for example, an upper silicon layer of asilicon-insulator-silicon stack of an SOI substrate). Alternatively, thefin structures 310 may be formed by a double-patterning lithography(DPL) process. DPL is a method of constructing a pattern on a substrateby dividing the pattern into two interleaved patterns. DPL allowsenhanced feature (e.g., fin) density. Various DPL methodologies may beused including double exposure (e.g., using two mask sets), formingspacers adjacent features and removing the features to provide a patternof spacers, resist freezing, and/or other suitable processes.

When etching the hard mask layer 306 and the substrate 302, any knownetching processes may be used, such as wet etching, dry etching, orplasma etching, but when an anisotropic etching is desired, a plasmaetching may be used. In one embodiment, etching the polymer may use amixture of process gases. For instance, oxygen and tetrafluoromethane(CF4), when mixed together for use in plasma etching, create theoxyfluoride ion (OF—). The oxyfluoride ion is a powerful etching agentfor polymeric substances. This ion is particularly adept at cutting thecarbon-carbon molecular bonds in the polymer backbone and removing themolecule quickly. The etchants that may be used for polymer etching mayinclude, but are not limited to, wet etchants such as potassiumhydroxide (KOH), ethylene diamine and pyrocatechol (EDP), orTetramethylammonium hydroxide (TMAH), or plasma etchants such as Cl₂,CCl₄, SiCl₂, BCl₃, CCl₂F₂, CF₄, SF₆, or NF₃.

After etching portions of the hard mask layer 306 and the siliconsubstrate 302, then the photoresist masks 304, which are no longerneeded, are removed by a process called an ashing. This process usuallyrequires a liquid “resist stripper”, which chemically alters the resistso that it no longer adheres to the hard mask layer 306. Alternatively,the photoresist masks 304 may be removed by a plasma containing oxygen,which oxidizes it. FIG. 3B shows the remaining portions of the hard masklayer 306 after the etching and ashing processes, which act as spacers306 for forming a layer of dielectric insulation among the finstructures 310 in the next step.

Also, FIG. 3B shows the fin structures 310 created being divided intotwo groups of multiple but equal numbered fin structures, 310 a and 310b, respectively formed adjacent two opposing ends of the substrate 302and spaced apart from each other by a distance greater than the averagespacing among the fin structures within each group, one for forming animplant region of a p-type thereon, and the other for forming an n-typeddoping region thereon in a subsequent step.

Next, at step 230, a plurality of dielectric strips 320 are formedwithin the trenches 315 defined among the fin structures 310 forinsulation, i.e., to electrically isolate the fin structures 310 fromone another, by utilizing isolation technology, such as local oxidationof silicon (LOCOS) or shallow trench isolation (STI). For that, adielectric material is deposited by spin-on coating or spin-ondielectric (SOD) process, CVD, or any other suitable depositionprocesses upon the fin structures 310, the hard mask spacers 306, andthe trenches 315 to form a dielectric layer. After the deposition, theupper portions of deposited dielectric layer may be removed by, in anembodiment, a Chemical Mechanical Polishing/Planarization (“CMP”)process down to the level of the top surfaces of the hard mask spacers306, as shown in FIG. 3C, completing the formation of the dielectricstrips 320 that are interwovenly disposed among the fin structures 310in each group, 310 a and 310 b, and in the region between the twogroups. The dielectric material used for the strips 320 may be thetypical undoped and doped silicon dioxide (SiO2), silicon oxynitride(SiON), silicon nitride (Si3N4), high-density plasma (HDP) oxides, TEOSoxides, high-k dielectric material such as a hafnium oxide (HfO₂),HfSiO, HfSiON, HMO, HMO, HfZrO, zirconium oxide, aluminum oxide, hafniumdioxide-alumina (HfO₂—Al₂O₃) alloy, titanium nitride (TiN), or any othersuitable materials, or combinations thereof. In some embodiments, thedielectric strips 320 may have a multi-layer structure such as a thermaloxide liner layer filled with silicon nitride or silicon oxide.

After formation of the plurality of dielectric strips 320, the spacers306 may be removed by an etching process, defining trenches 325 betweendielectric strips 320 and upon the fin structures 310 as shown in FIG.3D. Any known etching processes may be used, such as wet etching or dryetching. When an anisotropic etching is desired, a plasma etching may beused. The etchants may be any one that is known in the art such as Cl₂,CCl₄, SiCl₂, BCl₃, CCl₂F₂, CF₄, SF₆, or NF₃.

Next, at step 240, the substrate 302 is doped by a suitable implantationprocess as depicted in FIG. 3E. Here, the substrate 302 may be dopedwith any dopant known in the art, including p-type (P+) dopants orimpurities, such as boron or BF2, to form a p-type well, or n-type (N+)dopants or impurities, such as phosphorus or arsenic and/or combinationsthereof, to form an n-type well. Depending upon the type of dopants, thewell has two opposite conductivity types, i.e., electric conductioneither by electrons or holes, and the finished FinFET diode may becomeeither P-type or N-type. During the implantation process, the densityand penetration depth of dopants may be controlled such that althoughthe dopants are implanted through the fin structures 310 into thesubstrate 302, only the substrate 302 becomes primarily doped.

After finishing implantation of the substrate 302, the dielectric strips320 may be partially removed by a suitable etching process, defining finrecesses 335 between the fin structures 310 as shown in FIG. 3F. Anyknown etching processes may be used, such as wet etching or dry etching.When an anisotropic etching is desired, a plasma etching may be used.The etchants may be any one that is known in the art such as Cl₂, CCl₄,SiCl₂, BCl₃, CCl₂F₂, CF₄, SF₆, or NF₃.

Next, at step 250, one or more elongated gate structures 330 are formedover the fin structures 310 as depicted in FIG. 3G. The gate structures330 are substantially equal-spaced and parallel to one another, andextended perpendicular to the fin structures 310. In the presentdisclosure for a FinFET diode, the gate structures 330 are inactive ascontrasted to the FinFET transistors, but used to divide the elongateddoped semiconductor strips 340 to be subsequently formed upon the twogroups of the fin structures, 310 a and 310 b, into different sectionsfor enhancing the stability of the structure. The material used for thegate structures 330 may be the typical polysilicon or any other commonlyused metals such as Ni, Ti, Ta, Hf, and combinations thereof, metalsilicides such as NiSi, MoSi, HfSi, combinations thereof, and metalnitrides such as TiN, TaN, FIN, HfAlN, MoN, NiAlN, and combinationsthereof.

The gate structures 330 may be formed by any suitable process known inthe art, including deposition, photolithography patterning, and etchingprocesses. The deposition of a suitable gate material to form a gateelectrode layer may include chemical vapor deposition (CVD), physicalvapor deposition (PVD), atomic layer deposition (ALD), molecular beamepitaxy (MBE), high density plasma CVD (HDPCVD), metal organic CVD(MOCVD), remote plasma CVD (RPCVD), plasma enhanced CVD (PECVD),plating, other suitable methods, and/or combinations thereof. Thephotolithography patterning processes may include photoresist coating(e.g., spin-on coating), soft baking, mask aligning, exposure,post-exposure baking, developing the photoresist, rinsing, drying (e.g.,hard baking), other suitable processes, and/or combinations thereof.Alternatively, the photolithography exposing process may be implementedor replaced by other proper methods such as maskless photolithography,electron-beam writing, and ion-beam writing. The etching processes mayinclude dry etching, wet etching, and/or other etching methods (e.g.,reactive ion etching). After formation of a gate layer by deposition,any surplus of the gate layer in its upper part may be removed by aprocess of CMP.

In one embodiment, a gate dielectric layer may be further formed betweenthe gate structures 330 and the fin structures 310 by suitableprocesses. The dielectric material may include commonly used materialssuch as oxides, nitrides, oxynitrides, high-K dielectrics such as Ta₂O₅,Al₂O₃, HfO, SiTiO₃, HfSiO, HfSiON, or combinations thereof. In anotherembodiment, gate spacers (not shown) may be further formed on thesidewalls of the gate dielectric layer and gate structures.

Finally at step 260, a plurality of doped semiconductor strips 340 areformed, as source and drain (S/D) regions, upon the fin structures 310as shown in FIGS. 3H and 3I. The doped semiconductor strips 340comprises two groups, p-doped strips 340 a and n-doped strips 340 b,which are respectively formed upon the two groups of the fin structures,310 a and 310 b. Each of them has a similar elongated configuration asthe fin structures 310, extends lengthwise in parallel over the finstructures 310, being bordered by the previously formed gate structures330.

In one embodiment, the strips 340 may be formed via a selectiveepitaxial growth process. The epitaxy process may include chemical vapordeposition (CVD) including vapor-phase epitaxy (VPE) and/or ultra-highvacuum CVD (UHV-CVD), physical vapor deposition (PVD), molecular beamepitaxy (MBE), high density plasma CVD (HDPCVD), metal organic CVD(MOCVD), remote plasma CVD (RPCVD), Electro-less deposition, plating, orany suitable processes known in the art and/or combinations thereof.Such an epitaxial process may use either gaseous and/or liquidprecursors. The semiconducting material composing the strips 340 may be,in one embodiment, the same material as the fin structures 310 that areof the same material as the substrate 302 in the particular embodimentof the process depicted in FIGS. 3A-3I. In another embodiment, thesemiconducting material of the strips 340 may be different from that ofthe substrate 302. For example, if the resulting FinFET diode is aP-type, the material of the strips 340 may include silicon Germanium(SiGe), and if the resulting FinFET diode is a n-type, the material ofthe strips 340 may include silicon carbon (SiC).

During their formation by an epitaxial growth, the two groups of strips,340 a and 340 b, may be in-situ doped by any suitable implantationprocesses known in the art. They are doped respectively with p-typeimpurities, such as boron or BF2, and with n-type impurities, such asphosphorus or arsenic to form doped p-type and n-type regions. As isknown in the art, masks such as photo resists may be formed to coverregions not to be implanted. The impurity concentration may be betweenabout 10¹³/cm³ and about 10¹⁹/cm³, or even greater than 10²⁰/cm³ toproduce heavily doped regions. After the implantation process, one ormore annealing processes may be performed to activate the S/D regions.The annealing processes comprise rapid thermal annealing (RTA) and/orlaser annealing processes. In the resulting structure afterimplantation, a P-N junction is formed between either the P+ region orN+ region, comprising respectively the two groups of strips, 340 a and340 b, and the fin structures thereunder, depending on the type of thedoped well. For example, if the well is doped with p-type impurities(P-well), the P-N junction is formed between N+ doped group ofsemiconductors strips and the fin structures thereunder.

After formation of the doped strips 340 at step 260, a dielectricmaterial may be further deposited thereon by the spin-on coating orspin-on dielectric (SOD) process, CVD, or any other suitable depositionprocesses to electrically isolate the two groups of doped strips 340 aand 340 b from each other, and further, each of the strips from oneanother. The dielectric material may be the typical silicon dioxide(SiO2), silicon oxynitride (SiON), silicon nitride (Si3N4), high-densityplasma (HDP) oxides, TEOS oxides, high-k dielectric material such as ahafnium oxide (HfO₂), HfSiO, HfSiON, HfTaO, HfTiO, HfZrO, zirconiumoxide, aluminum oxide, hafnium dioxide-alumina (HfO₂—Al₂O₃) alloy,titanium nitride (TiN), or any other suitable materials, or combinationsthereof.

In the embodiment shown in FIGS. 3A-3I, the doped semiconductor strips340 are formed by an epitaxial growth after the fin structures 310 havebeen formed by etching processes. In another embodiment (not shown),however, the fin structures themselves may be formed by an epitaxialgrowth upon a planar substrate, rather than being formed out of thesubstrate by an etching process. In that embodiment, the dopedsemiconductor strips may be formed simultaneously with the finstructures as an integral part of them by the epitaxial growth, whilebeing in-situ doped.

Lastly at step 270, one or more metal contacts are formed upon the twogroups of doped strips 340 a and 340 b for providing a forward biasbetween the S/D regions. The contacts may be formed by a salicide(self-aligned silicide) process, which involves deposition of atransition metal to form a thin layer via a suitable process such asCVD, application of heat to allow the transition metal to react withexposed silicon in the active regions (source and drain) to form alow-resistance transition metal silicide, and removal of any remainingtransition metal by chemical etching, leaving silicide contacts only inthe active regions. The typical transition metal may include nickel,cobalt, tungsten, tantalum, titanium, platinum, erbium, palladium, orcombinations thereof.

FIG. 4 is a schematic top plan view of a FinFET diode 400 made in anaspect of the present disclosure. The FinFET diode 400 largely comprisesa substrate 402 having two opposing ends, two groups of substantiallyparallel elongated semiconductor fin structures 410 and 420, three pereach group, respectively formed adjacent the two opposing ends upon thesubstrate 402, substantially equal-spaced and parallel elongated gatestructures 430 formed upon the fin structures 410 and 420, each of whichtraverses both group fin structures 410 and 420 perpendicularly, twooppositely doped (p-doped and n-doped) areas or groups of semiconductorstrips, 440 and 450, respectively formed upon the fin structures 410 and420, and metal contacts 460 formed upon and adjoined with the two dopedareas or groups of strips, 440 and 450. The doped areas or groups ofstrips, 440 and 450, are divided into different sections by theperpendicularly traversing gate structures 430, and in each section,there exists one pair of electrically disconnected metal contacts 460,each of which is in contact with and adjoining all doped strips in thesame respective groups, 440 and 450.

The two oppositely doped areas 440 and 450 are separated from each otherby a separation greater than the mean inter-spacing among the finstructures 410 and 420 and insulated by a dielectric material fillingthe separation. In the embodiment shown in FIG. 4, the fin structureswere formed first all equal spaced, and the doped semiconductor regionshave been subsequently formed thereupon. In this case, there may be afew fin structures 415 present in the separation, which carries no dopedmaterial. FIG. 4 also shows the two doped areas or strips 440 and 450being divided into several periodic sections by the gate structures 430.Such sectioning of the doped strips may be desirable to ensure thestructural stability of during and after the formation of the dopedsemiconductor strips 440 and 450 in accordance of the process describedin FIGS. 3A-3I.

FIG. 5 is a perspective cross-sectional view of a FinFET diode 500 madein an embodiment of the present disclosure. The view is obtained bycutting the FinFET diode 400 in FIG. 4 along the plane A-B. Thedifference is that in the FinFET diode 500, there is shown only one finstructure for each of the two oppositely doped regions, while in theFinFET diode 400 there are shown three. The FinFET diode 500 has twoelongated parallel fin structures 410 and 420, formed upon a substrate402 doped with p-type dopants to form a P-well, (which may be doped withn-type dopants to form N-well), two elongated oppositely dopedsemiconductor strips 440 and 450, respectively formed upon the two finstructures 410 and 420, STI of dielectric material 470 separating andinsulating the fin structures 410 and 420 from each other, as well asthe doped semiconductor strips 440 and 450 from each other, two metalcontacts 460 formed upon, and adjoined with, the two doped semiconductorstrips 440 and 450, respectively, and an elongated gate structure 430formed upon, but extending perpendicularly across the fin structures 410and 420. The traversing gate structure 430 would mark ends of the twodoped semiconductor strips 440 and 450. In the separation between thetwo fin structures 410 and 420, there may be a few pre-formed, un-dopedfin structures 415 having a shortened height by an etching process.

In the particular embodiment shown in FIG. 5, the substrate 402 is dopedto form a P-well, and the P-N junction would be formed between the N+doped semiconductor strip 450 and the fin structure 420 thereunder, andthe injection current would flow the P+ doped region (semiconductorstrip 440) to the N+ doped semiconductor strip 450 through the well asindicated by the arrow in FIG. 5.

In the prior art FinFET diode, schematically shown in FIG. 1B, theentire section of fin structures, defined as the region between twoneighboring gate structures, is doped with a same type of impurities toform either a p-type or n-type section, and in this structure, the P-Njunction is formed between two such sections that are set apart andoppositely doped. By contrast, in the high efficiency FinFET diode inthe present disclosure, schematically shown in FIGS. 4 and 5, eachsection of fin structures between two neighboring gate structures isdivided into two separated and oppositely doped regions, P+ and N+regions. In this structure, the P-N junction is formed between themwithin each section. Also, as contrasted to the prior art FinFET diodein FIG. 1B, in which the metal contacts runs through the entire finstructures in one section, the metal contacts 460 in the high efficiencyFinFET diode of the present disclosure are disconnected in the middle ofeach section to run only within the two respective doped regions.

The FinFET diode made according to the present disclosure, described inFIGS. 2-5, is found to overcome the reduced active area problem presentin the prior art FinFET diode, and produce higher efficiency. FIGS. 6Aand 6B show computer simulation results for the efficiencies of variousembodiments of the FinFET diodes in the present disclosure. Thesimulations were performed by calculating the injection currentsproduced by FinFET diodes having 2, 4, 6, 8, and 12 fin structures in aunit cell, defined by a section bordered by two neighboring gatestructures in FIG. 4 and including two oppositely doped regions. In thesimulation, the FinFET diodes to be compared were set to have a sametotal number of fin structures to ensure that all have the sameeffective area of active region. Accordingly, each diode is subject tohave different total cell area, comprising different number of unitcells. The efficiency of a diode in this simulation has been defined tobe injection current produced, divided by the total cell area. In alldiodes, the ratio of the width of STI region, shown in FIG. 3, to thewidth of a fin structure was set to between 10˜16 and the forward biaswas set to be 1.5 V. As shown in the table of simulation results, FIG.6A, and its plot in FIG. 6B, the FinFET diode made according to anaspect of the present disclosure has been found to be optimized, i.e.,have the best efficiency, when the number of fin structures in each unitcell is 4, 6, and 8.

The FinFET diode manufactured according to a method in the presentdisclosure provides advantages over the FinFET diodes used in the priorart. It produces higher efficiency by mitigating the degradation problemin the conventional FinFET diodes due to the reduced active area for thepresence of fin structures. Further, the method in the presentdisclosure provides a way of optimizing the FinFET diodes as varying thenumber of fin structures in a unit cell or other parameters such asbias, or STI width to fin width ratio. The FinFET diodes manufactured inthe present disclosure may be used for an ESD (electrostatic discharge)diode in ESD protection circuits, or in any other types of applicationknown in the art.

The foregoing outlines features of several embodiments so that thoseskilled in the art may better understand the aspects of the presentdisclosure. Those skilled in the art should appreciate that they mayreadily use the present disclosure as a basis for designing or modifyingother processes and structures for carrying out the same purposes and/orachieving the same advantages of the embodiments introduced herein.Those skilled in the art should also realize that such equivalentconstructions do not depart from the spirit and scope of the presentdisclosure, and that they may make various changes, substitutions, andalterations herein without departing from the spirit and scope of thepresent disclosure.

What is claimed is:
 1. A semiconductor device comprising: a substratehaving opposing first and second ends; first and second groups of one ormore substantially parallel, elongated, equal numbered semiconductor finstructures disposed upon the substrate adjacent the first and the secondends, respectively, the first and second groups being spaced apart fromeach other; one or more substantially equal-spaced and parallelelongated gate structures formed upon the first and the second group finstructures such that each gate structure traverses both the first andthe second group fin structures perpendicularly; a plurality ofdielectric strips interwovenly disposed among the first and the secondgroups of fin structures for electric insulation from one another; afirst group of one or more doped semiconductor strips having a firstconductivity type and formed lengthwise upon the first group finstructures, respectively; and a second group of one or more second dopedsemiconductor strips having a second conductivity type opposite thefirst conductivity type and formed lengthwise upon the second group finstructures, respectively, wherein the first group semiconductor stripsare electrically insulated from the second group semiconductor strips.2. The semiconductor device of claim 1, wherein each of the first andthe second groups of semiconductor strips is sectioned by the gatestructures.
 3. The semiconductor device of claim 1, further comprisingone or more metal contacts formed upon the first and the second groupsof semiconductor strips.
 4. The semiconductor device of claim 3, whereinall semiconductor strips in the first group are electrically connectedto one another via the metal contacts.
 5. The semiconductor device ofclaim 1, wherein the substrate is implanted with a dopant of either thefirst conductivity type or the second conductivity type.
 6. Thesemiconductor device of claim 1, wherein the first and the second groupsof semiconductor strips are integrally formed with the respective firstand second group fin structures by epitaxial growth.
 7. Thesemiconductor device of claim 1, wherein the first and the second groupsof semiconductor strips are in-situ doped.
 8. The semiconductor deviceof claim 1, wherein the number of the fin structures in a unit cell is4, 6, or
 8. 9. A FinFET diode comprising: a semiconductor substratedoped to have either a first conductivity type or a second conductivitytype opposite the first conductivity type; a first group and a secondgroup of substantially equal-spaced, parallel, elongated, and equalnumbered semiconductor fin structures formed over the substrate, thefirst and second groups being spaced-apart and electrically insulatedfrom each other, and the fin structures in each group being electricallyinsulated from one another; and a plurality of substantiallyequal-spaced and parallel elongated gate structures formed upon thefirst and the second groups of fin structures such that each gatestructure traverses both the first and the second groups of finstructures perpendicularly, wherein a top portion of each of the firstgroup fin structures is doped to have the first conductivity type and atop portion of each of the second group fin structures is doped to havethe second conductivity type.
 10. The FinFET diode of claim 9, whereinthe top portions of the first and the second groups of fin structuresare sectioned by the gate structures.
 11. The FinFET diode of claim 9,further comprising one or more metal contacts formed upon the doped topportions of the first and the second groups of fin structures.
 12. TheFinFET diode of claim 9, wherein the spacing between two closest finstructures, each of which is respectively from the first and secondgroups, is greater than the average spacing between two adjacent finstructures within the respective first and second groups.
 13. The FinFETdiode of claim 9, wherein the number of the fin structures in a unitcell is 4, 6, or
 8. 14. A FinFET diode comprising: a semiconductorsubstrate doped to have a first conductivity type; a first plurality ofsubstantially parallel, elongated fin structures formed over thesubstrate, each fin structure in the first plurality of fin structureshaving a semiconductor strip of the first conductivity type extendinglengthwise thereon; a second plurality of substantially parallel,elongated fin structures formed over the substrate, the second pluralityof fin structures being spaced from and electrically insulated from thefirst plurality of fin structures, and each fin structure in the secondplurality of fin structures having a semiconductor strip of a secondconductivity type extending lengthwise thereon, wherein the secondconductivity type is opposite of the first conductivity type; a firstelongated gate structure formed upon and perpendicularly traversing boththe first and second plurality of fin structures; and a second elongatedgate structure formed upon and perpendicularly traversing both the firstand second plurality of fin structures, the second elongated gatestructure being spaced from the first elongated gate structure.
 15. TheFinFET diode of claim 14, wherein the semiconductor strips of the firstand the second pluralities of fin structures are sectioned by the firstand second gate structures.
 16. The FinFET diode of claim 14, furthercomprising one or more metal contacts formed upon the semiconductorstrips of the first and second pluralities of fin structures.
 17. TheFinFET diode of claim 14, wherein the spacing between two closest finstructures, each of which is respectively from the first and secondpluralities of fin structures, is greater than the average spacingbetween two adjacent fin structures within the respective first andsecond pluralities of fin structures.
 18. The FinFET diode of claim 14,wherein the number of the fin structures in the first plurality of finstructures is one of 4, 6, and
 8. 19. The FinFET diode of claim 14,wherein the semiconductor strips are integrally formed with therespective fin structures of the first and second pluralities of finstructures by epitaxial growth.
 20. The FinFET diode of claim 14,wherein the fin structures in the first plurality of fin structures areelectrically isolated from one another.